Neoizol
ROLLING WATERPROOFING MATERIAL
APPLICATION AREA:
It is designed for waterproofing construction structures operated in all climatic regions in accordance with SNiP 23-01, as a backing layer for the construction of pitched roofs from flexible tiles
NEOIZOL OS
on a non-rotting basis, on both sides of which a bitumen-polymer binder with a polymer film and / or sand is applied on the upper side of the web and with an anti-adhesive polymer film or paper from the underside of the web.
NEOIZOL GL
on the basis of a glass wool, on both sides of which there is a bitumen binder with sand on the upper side of the canvas and sand or fine-grained sprinkling from the underside of the canvas.
TECHNICAL CHARACTERISTICS |
|
NEOIZOL OS BITUMENOUS-POLYMER SELF-ADHESIVE |
NEOIZOL GL BITUMENOUS-POLYMER |
Weight of 1 sq.m. material, kg, in the range of |
|
1,0-5,0 |
1,0-3,0 |
Base weight, g / m2, not less than |
|
40 |
40 |
Resistance to tearing the adhesive joint, kN / m (kgf / cm) |
|
0,5(0,5) |
|
Temperature of brittleness of the binder, K (oC), not higher than |
|
248(минус.25) |
258(минус.15) |
Heat resistance for 2 hours, at a temperature, oС |
|
+85 |
+100 |
Water absorption within 24 hours, %, by weight, no more than |
|
1 |
1 |
Flexibility |
when tested on a rod with a radius, mm |
25 |
25 |
|
on the surface of the sample there should be no cracks at a temperature, oС, no higher than |
-15 |
-15 |
Strength of adhesion Mpa (kgf / cm) at least |
-with concrete |
0,2(2,0) |
– |
|
-with steel |
0,2(2,0) |
– |
Breaking strength at tension H (kgf): - fiberglass polyester non-woven fabric |
|
394 500 |
394 500 |
Shear strength of adhesive joint KN / m (kgf / cm) |
|
|
|
length of pallet | 1,2 m |
width of pallet | 1m |
number of rolls per pallet | 25 rolls |
- roof waterproofing